I. Suggestions on lithium iron phosphate battery manufacturing formulation:LifePo4: SP: KS-6: PVDF: NMP = (90-92): (1-2): (2-1): (5-6) :( 120-140)
Second, mixed recommendations for ingredients of lithium iron phosphate battery:
1.) PVDF mother liquor formulation, 5% PVDF NMP solution, when dissolved PVDF mother liquor, must be fully dissolved, * Good energy (50-60 degrees) stir for one hour, and stand for 2 hours, make high The molecular chain is sufficiently stretched, and the film formation performance * is good.
2.) Add KS-6 to the configured mother liquor, and thoroughly wet and stir at high speed for 1 hour to make it sufficiently dispersed. The lubrication of the sheet graphite is prepared for the dispersion of the next SP and main material.
3.) In the above solution, SP is sufficiently wet, stirred at high speed for one hour, fully dispersed, stirred at low speed and evaporate, eliminate the addition introduced by SP.
4.) In the above solution, it is necessary to add a lithium iron phosphate, sufficient humid, high speed (3,500 rpm, line speed 350-500), then add half of the remaining material, stirred at high speed 60 Minute, add 20% -40% of the solid material mass
NMP, stirred for 30 minutes, after the viscosity was lowered, and the remaining material was added, stirred at high speed for 2-3 hours. Add the appropriate amount of NMP to adjust the viscosity of the slurry, stir slowly and evacuate.
Wuxi Huizhong, Nanjing Xia Hua, Wuxi Recommend: LiFePO4 Battery Manufacturer Energy storage battery Manufacturer Integrated machine energy storage battery series Manufacturer Lead lithium battery Manufacturer Outdoor Backup Battery Manufacturer Portable outdoor power supply Manufacturer Power battery Manufacturer Powerwall LiFePO4 Battery Manufacturer Battery rack Manufacturers Telecom LiFePO4 Battery Manufacturer Wall mounted battery storage Manufacturer China Lifepo4 Battery